Code: REP.0068
Components: 1
Appearance: Powder
Thixotropic, reinforced fibre, anti-shrink mortar, slightly expansive in plastic phase, high-performance in terms of resistance and waterproofing characteristics, specific for the compensation of cavities and detachments in roughcast underpinning, and for accurate fixing of wooden or steel beams in masonry whatever its nature.
Pot-life: 60 min
Max. recommended thickness: 8 cm
Nonflammable
Use wearing protective gloves
Temperature of use: +5 / +35 °C
Mix with water: 12-13 %
Maximum diameter of aggregate: 2 mm
Min. recommended thickness: 1 cm
Shelf-life: 12 months
Chloride content
< 0.01 %
Darcy impermeability
10⁻⁹ cm/s
Flexural strength at 01 day
6 N/mm²
Compressive strength after 28 days
60 N/mm²
Bonding force
> 2 MPa
Static elastic modulus
25.000 N/mm²
Contrasted expansion with air curing for 1 day
> 0.6 mm/m
Compressive strength after 01 day
30 N/mm²
Determination of thermal compatibility
> 2 MPa
Capillary absorption
0.45 kg•h^0.5/m²
pH
>12 _
Flexural strength after 28 days
9 N/mm²
Density
2100 kg/m³
- Gray
- Bag 25 kg
- Pallet: 50 x (Bag 25 kg)
REPAR TIX G2 is based on high-resistance cements, superpozzolanic fillers, plasticisers, stabilisers, and anticorrosive agents, antiallergic additives, selected aggregates. Free of chloride, aluminium, metal powders and aggressive substances in general.
Approximately 19 kg/m² of REPAR TIX G2 for every centimetre of thickness to be implemented (approximately 1900 kg per cubic metre).
Fixing and anchorages of I-beams, clamps, beams, metal structures, reinforcing rods, prefabricated elements etc. Execution of render underpinning, in civilian, industrial, rural and infrastructural building, both for restructuring and newly built.
Application surfaces should be clean, free of soiling, crumbling and non-adhering parts, dust, etc., conveniently saturated with water until they reach the condition "saturated with dry surface". An adequate roughening of the surfaces by scarifying, sandblasting etc. is always necessary in order to obtain the maximum adhesion values to the substrate. The optimal values are obtained with high pressure hydro-scarification. Bare the irons undergoing disruptive oxidation or deeply oxidized, removing the rust of the exposed irons (by sandblasting or abrasive brushes).
Pour about 2/3 of the mixing water into the mixer, add REPAR TIX G2 and the remaining water; continue to mix until a homogeneous lump-free mixture is obtained. The mixing water should be about 12-13% of the weight of the bag. After mixing is completed wait a few minutes before applying.
For high anchoring sections add GHIAIETTO 6.10 (please refer to the appropriate technical data sheet for more information).
- Brick trowel
- Finishing trowel
- Spatula
- Water
- Bricks
- Concrete
- Mixed walls (bricks and stones)
- Prefabricated concrete
- Stone walls
Adopt laying procedures capable of ensuring the absence of gaps and discontinuities; cure the protection and the prolonged moist hardening of exposed surfaces.
Want to know more about our products?
REPAR TIX
Structural, thixotropic, fibre reinforced monocomponent cement mortar It is classic mortar for renovation of concrete, efficient, reliable and cheap!
REPAR TIX BIC
Structural, thixotropic, fibre reinforced, two-component cement mortar Compared to REPAR TIX it is more adhesive with high waterproofing and moderately deformable.
REPAR TIX SFR
Monocomponent, thixotropic structural cement mortar, with added elastic metal fibres. Specifically for non-reinforced grout of considerable thickness, also in aggressive or high humidity environments.
REPAR TIX HG
Structural, thixotropic, fibre reinforced, monocomponent cement mortar with high performance. Specifically for marine, mountain and aggressive environment applications in general. Also ideal for wet shotcrete. Highly recommended!
REPAR TIX SPEEDY HP
Super rapid hardening mortar (about 20 '), specific for maintenance works on road works and the like.