A structural and shrinkage-compensated thixotropic cementitious mortar with a maximum aggregate grain size of 0.6 mm, consisting of high-strength cements, super-pozzolanic fillers, stabilising additives and high-tenacity polypropylene microfibres. The fine grain size and exceptional workability of the mortar render REPAR TIX FINE particularly suited to cortical restorations of structures (with the maximum thickness of the single coat being 20 mm) on reinforced concrete and masonry works, for the restoration of concrete requiring an excellent level of surface finishing, operations on the intrados of slabs, even in environments with aggressive exposure (marine, industrial). Manual or spray application with wet curing for the first 48–72 hours.
Products and systems for the protection and repair of concrete structures - Structural and non-structural repair (R4)
Max. recommended thickness: 20 mm
Maximum diameter of aggregate: 0.5 mm
Min. recommended thickness: 2 mm
Mix with water: 18-19 %
Pot-life: 60 min
Shelf-life: 12 months
Temperature of use: +5 / +35 °C
Use wearing protective gloves
> 2 N/mm²
> 50 N/mm²
1 x 10 E-10 cm/s
Determination of thermal compatibility
> 6 N/mm²
> 12.5 _
Reaction to fire
Resistance to carbonatation
Static elastic modulus
> 20000 N/mm²
- Bag 25 kg
- Pallet: 50 x (Bag 25 kg)
The fine grain size of the premix (maximum grain 0.5 mm) allows a very accurate level of finish and surface smoothing. The structural thixotropic mortar REPAR TIX FINE can be advantageously added with 0.25% of FLUID SRA, a special additive capable of reducing both plastic shrinkage and hydraulic shrinkage. FLUID SRA in fact protects the curing of the mortar and, when mixed with REPAR TIX FINE, it can be considered a technologically advanced system capable of reducing the rapid evaporation of water from the mortar and promoting the development of hydration reactions. FLUID SRA, thanks to the interaction with some components of the cement, allows to obtain final shrinkage from 20 to 50% lower than the standard values of the REPAR TIX prepared with the addition of water alone.
Approximately 18 kg / m² of REPAR TIX FINE for each centimeter of thickness to be created (approximately 1800 kg for each cubic meter).
Structural smoothing. Restoration, repairs, reconstruction of the concrete cover, construction of reliable and durable coatings of building, civil, hydraulic, industrial, concrete and masonry works.
The application surfaces must be clean, free of dirt, crumbly and incoherent parts, dust, etc., saturated with "saturated dry surface" water. Adequate roughening of the surfaces by scarifying, sandblasting etc. is always necessary in order to obtain the maximum adhesion values to the substrate. The optimal values are obtained with high pressure hydro-scarification. Bare the irons undergoing disruptive oxidation or deeply oxidized, removing the rust of the exposed irons (by sandblasting or abrasive brushes). Before restoring them, it is recommended to apply the consolidating re-alkalizing CONSILEX SAN on exposed surfaces.
Pour 2/3 of the total mixing water into the mixer (about 2.5 liters per bag), gradually add the product and the remaining water, until a homogeneous mixture of the desired consistency and free of lumps is obtained. Take care of the protection and the damp curing of the exposed surfaces.
The addition of BOND HG to the mixing water (in the ratio of about 0.5-0.7 kg per bag of product) allows significant improvements in terms of adhesiveness, adhesion, impermeability, workability, moldability and deformation capacity .
High coating thicknesses, static requirements, monolithic requirements, etc. they may make it necessary to use suitable reinforcements (electro-welded meshes, etc.) anchored to the substrate with SYNTECH PROFIX, SYNTECH FIX EP or GROUT CABLE.
- Brick trowel
- Finishing trowel
- Shotcrete machine
- Plastering machine
- Prefabricated concrete
- Mixed walls (bricks and stones)
- Stone walls
- Rock walls