REPAR TIX BIC
Thixotropic, rheoplastic, structural, two-component fibre reinforced mortar
Code: REP.0134
Components: 2
Appearance: Liquid + Powder
Structural cementitious mortar, two-component, composite, with compensated shrinkage, fiber-reinforced, based on high-strength cements, super-pozzolanic fillers, water-dispersed polymeric resins, migratory corrosion inhibitors, anti-shrinkage additives, plasticizers, stabilizers and anticorrosion agents, selected aggregates, READYMESH microfibers in glass, with a high zirconium content, and multifilament polypropylene.
Customs Code
Linee di appartenenza
Certification obtained and Standards
EN 998-1
Specification for Mortar for Masonry - General purpose rendering/plastering mortar (GP)
EN 1504-3
Products and systems for the protection and repair of concrete structures - Structural and non-structural repair
General characteristics
Temperature of use: +5 / +35 °C
Shelf-life: 12 months
Maximum diameter of aggregate: 1.5 mm
Min. recommended thickness: 3 mm
Pot-life: 60 min
Max. recommended thickness: 3 cm
Technical specifications
Compressive strength after 07 days
> 40 N/mm²
Bonding force
2.3 N/mm²
Static elastic modulus
16000 N/mm²
pH
> 12 _
Flexural strength after 28 days
9 N/mm²
Compressive strength after 28 days
> 50 N/mm²
Reaction to fire
B-s2 d0 _
Capillary absorption
0.34 kg•h^0.5/m²
Coefficient of permeability
22.1 μ
Average carbonation depth
3.7 mm
Flexural strength after 07 days
7.5 N/mm²
Density
2125 kg/m³
Chloride content
0.01 %
Darcy impermeability
1 x 10 E-10 cm/s
Flexural strength at 01 day
> 4 N/mm²
Compressive strength after 01 day
> 18 N/mm²
Available colours
- Gray
Packaging and dimensions
- Bag 25 kg [A]
- Kit: 1 Bag 25 kg [A] + 1 Plastic can 5 kg [B]
- Plastic can 5 kg [B]
Characteristics
After mixing the two components, REPAR TIX BIC is perfectly workable with manual methods or with spraying machines. The applied and hardened material will have very high adhesion, durability, impermeable to water, with good vapor permeability, high physical-mechanical resistance (class R3 according to UNI EN 1504/3). The product also has a particularly low elastic modulus and contains migratory corrosion inhibitors in its B component.
The thixotropic characteristics of the product allow excellent adhesion and easy spreadability on vertical surfaces, on the lower parts of beams, shelves or slabs, often even on structures indirectly subjected to light vibrations or dynamic stresses during application. It solves the problems of complex reconstructions or restorations, even on difficult-to-grip substrates and for a wide range of applied thicknesses: from a minimum of 3 mm (to be spread with a blade and finished with a trowel) to a maximum of 100 mm. and beyond, naturally in succession of layers of 25-30 mm / each. (for large thicknesses on large surfaces it is always advisable to provide a contrasting net on connectors fixed to the support). It does not require wetting or anti-evaporation protection after application. The superpozzolanic reaction of the peculiar reactive fillers contained in component A, the three-dimensional micro-armor provided by a balanced mix of READYMESH fibers, together with the special polymers and migratory corrosion inhibitors contained in component B, guarantee the hardened product very strong adhesion to the substrate, dimensional stability and maximum durability to environmental aggressions (from carbonation, acid rain, chlorides, sulphates).
Consumption
Approximately 20 kg/m² of REPAR TIX BIC for every centimetre of thickness to be implemented (approximately 2000 kg per cubic metre).
Use fields
For any type of repair or restoration on deteriorated concrete and masonry. Restoration, structural recovery, reconstruction of the concrete cover, construction of reliable and durable coatings of civil, hydraulic, industrial, concrete and masonry building works, even in particularly aggressive exposure environments (XC2, XC3, XC4, XD1, XD2, XD3, XS2, XS3, XA1, XA2, XA3, XF2, XF4)
Preparation of supports
Application surfaces should be clean, free of dirt, crumbling and non-adhering parts, dust etc., and saturated with water "saturated with dry surface".. An adequate roughening of the surfaces by scarifying, sandblasting etc. is always necessary in order to obtain the maximum adhesion values to the substrate. The optimal values are obtained with high pressure hydro-scarification. Uncover the irons undergoing disruptive oxidation or deeply oxidized, removing the rust of the exposed irons (by sandblasting or abrasive brushes)
Use method
Pour component B (liquid) into a container (bucket or other), gradually add and mix in component A (powder), continue to mix until the mixture is totally lump-free. The optimal consistency of the product and the consequent physical-mechanical performances declared in this technical data sheet can be reached using 4.5 kg of COMPONENT B for each 25 kg bag. The excess quantity of COMPONENT B (0.5 kg) is particularly useful for priming the substrate, or for wetting the trowel in the final smoothing operation, or in hot and arid environmental conditions where the mixed product is kept at rest in the bucket it may require some light addition of liquid to regain its optimal consistency, thus avoiding uncontrolled water additions.
Provide reconstruction thicknesses in the range 3 to 30 mm; for greater thicknesses add 3-6 mm gravel (add up to 30% by weight of the initial compound). High coating thicknesses, static monolithic requirements, etc., it may be necessary to resort to appropriate reinforcements (electrowelded mesh etc.) anchored to the support with SYNTECH PROFIX or GROUT MICROJ or REPAR TIX G2.
Application methods
- Brick trowel
- Finishing trowel
- Plastering machine
- Shotcrete machine
- Spatula
Tool cleaning
- Water
Permitted supports
- Concrete
- Fiber-cement
- Mixed walls (bricks and stones)
- Prefabricated concrete
- Stone walls
Warnings, precautions and Ecology
Thermal range of application and conservation: +5 / +35 °C, does not apply in case of direct exposure to sunlight. Cure the protection and the moist hardening of exposed surfaces.
Contact us now
Want to know more about our products?
Share
Technical Data Sheet [ITA]
Technical Data Sheet [ESP]
Technical Data Sheet [POR]
Technical Data Sheet [DEU]
Technical Data Sheet [FRA]
Technical Data Sheet [RUM]Alternative products
REPAR TIX G2
Thixotropic cement mortar, shrink-proof, moderately expansive. Specifically for the filling of vacuums in the grouting of metal or wooden structures on vertical walls.
REPAR TIX
Structural, thixotropic, fibre reinforced monocomponent cement mortar It is classic mortar for renovation of concrete, efficient, reliable and cheap!
REPAR TIX SFR
Monocomponent, thixotropic structural cement mortar, with added elastic metal fibres. Specifically for non-reinforced grout of considerable thickness, also in aggressive or high humidity environments.
REPAR TIX HG
Structural, thixotropic, fibre reinforced, monocomponent cement mortar with high performance. Specifically for marine, mountain and aggressive environment applications in general. Also ideal for wet shotcrete. Highly recommended!
REPAR TIX SPEEDY HP
Super rapid hardening mortar (about 20 '), specific for maintenance works on road works and the like.