Premixed monocomponent powder compound, based on hydraulic binders, water-dispersible resins, selected siliceous and calcareous aggregates, specific agents, for the packaging, with the sole addition of water, of an adhesive thixotropic mortar for fine smoothing of elements in concrete, cementitious plasters, bastard mortar, plastic scratched, tiled coatings, HPFRC conglomerates and the bonding of expanded polystyrene and polystyrene insulation to masonry or old plaster, and polystyrene and glass fiber nets in the RINFOR SYSTEM 3 anti-tip system.
Specification for Mortar for Masonry - General purpose rendering/plastering mortar (GP)
Max. recommended thickness: 5 mm
Maximum diameter of aggregate: 0.6 mm
Min. recommended thickness: 2 mm
Mix with water: 18-20 %
Pot-life: 120 min
Shelf-life: 12 months
Temperature of use: +8 / +30 °C
Use wearing protective gloves
> 1.5 N/mm²
Compressive strength after 01 day
> 4 N/mm²
Compressive strength after 07 days
Compressive strength after 28 days
> 20 N/mm²
Flexural strength after 28 days
> 6 N/mm²
- Bag 25 kg
RASOCOAT is a gray color normal hardening smoothing compound with a maximum grain size of 0.6 mm, fiber-reinforced with READYMESH PM polypropylene microfibers. The particular composition gives the mortar obtained, by mixing RASOCOAT with water only, high adhesive power even on difficult surfaces, high smoothness in application with a smooth trowel and easy surface finishing with a metal trowel or sponge float.
As an adhesive: approximately 5.5 kg/m². As a reinforced skim: from 3 to 4 kg/m² in normal skimming coats, from 8 to 10 kg/m² in skimming coats for the RINFOR SYSTEM 3 anti-tip system.
Regularization and finishing of concrete walls, cement-based plasters or cement-lime mortar, before painting. Smoothing of plastic scratched as long as they are consistent, clean and well anchored to the substrate. Smoothing of tiled walls as long as they are firmly anchored to the substrate and after careful cleaning. Skimming of mineral wood panels (Eraclit® type). Smoothing of HPFRC conglomerates and very low porosity mortars. Realization of smoothing, coatings and gluing in thermal insulation systems, including constructions with expanded polystyrene panels. Skim coat capable of transferring stresses and incorporating ARMAGLASS STRUCTURA fiberglass meshes in the RINFOR SYSTEM 3 anti-tipping masonry system.
The application surfaces must be clean, free of dirt, crumbly and incoherent parts, dust, etc. If the substrate consists of a scratched plastic or tiles, these must be consistent and well adherent to the substrate. Wash all the surfaces subject to the intervention with water in order to eliminate dusty residues that prevent proper adhesion. Absorbent substrates, such as plasters or concrete, must be thoroughly moistened with water, while substrates that are not porous or not porous, consisting of scratched plastic, tiles or HPFRC conglomerates, must be dry at the time of application. In any case, remove the surface water veils with compressed air or rags.
Pour 2/3 of the total mixing water into the mixer, then gradually add the product and the remaining water, mixing until a homogeneous mixture of the desired consistency and free of lumps is obtained. Let the mixture rest for about 1 minute and then proceed with a further short mixing. Spread with a blade, smooth or notched metal trowel in the manner specific to the specific application and paying attention to the following procedures:
- In the application of gluing the polystyrene panel, wait at least 24 hours (at 20 ° C), before proceeding to the following processing (smoothing, etc.).
- In smoothing applications, do not exceed the overall thickness of 4 mm for each coat. The use of the ARMAGLASS 160 alkaline-resistant fiberglass mesh is recommended. The mesh must be pressed with a smooth spatula on the still fresh mix, with the warning to create overlaps of at least 10 cm between the different mesh sheets (or in the joints between one panel and the next in the case of smoothing on heat-insulating panels). Once the first layer of RASOCOAT has dried, proceed with the uniform application of the next layer.
The consumption for gluing the panels is about 5-6 kg / m². Consumption for a normal two-coat reinforced leveling coat with a total thickness of 2 mm is approximately 3-4 kg / m².
Consumption for reinforced leveling compounds in anti-tipping systems is approximately 8-10 kg / m².
- Brick trowel
- Finishing trowel
- Sponge float
- Notched finishing trowel
- Cement-based or lime-based mortars
- Stone walls
- Thermal insulating panels
- Acrylic wall coatings
Vuoi saperne di più sui nostri prodotti?
Two-component cement adhesive designed specifically for casting tiles, even with low absorption, on waterproof surfaces with osmotic cement or on concrete surfaces.
Azichem's leading product in the natural adhesives sector, specifically for ecological building work. Also an excellent adhesive/finishing coat for natural, modular panels.
Universal adhesive for tiles of any kind (except wood), for vertical or horizontal surfaces, for indoors and outdoors. Azichem's adhesive bestseller. Recommended!