Code: GRT.0069
Components: 1
Appearance: Powder
Castable mortar, reinforced with steel fibres, fast-curing, based on portland cement, special binders, selected siliceous aggregates and specific rheologic agents, for repairs, reconstructions and anchorages for fast re-use, in road works and in concrete, even in severe weather conditions and at low temperatures.
EN 1504-3
Products and systems for the protection and repair of concrete structures - Structural and non-structural repair (R4)
UV-resistant
Maximum diameter of aggregate: 5 mm
Mix with water: 12 - 14 %
Pot-life: 8 - 10 min
Quick setting product
Min. recommended thickness: 2 cm
Shelf-life: 12 months
Use wearing protective gloves
Temperature of use: +3 / +25 °C
Nonflammable
Chloride content
< 0.01 %
Flexural strength at 01 day
> 6 N/mm²
Flexural strength after 28 days
> 13 N/mm²
Resistance to carbonatation
> reference concrete _
Static elastic modulus
30000 N/mm²
Thermal compatibility
> 2 MPa
Density
2300 kg/m³
Capillary absorption
0.5
> 35 N/mm²
Compressive strength after 28 days
> 80 N/mm²
- Black
- Gray
- Bag 25 kg
- Pallet: 50 x (Bag 25 kg)
Approximately 21,50 kg/m² of GROUT 447 SFR for every centimetre of thickness to be implemented (approximately 2150 kg per cubic metre).
Repairs, reconstructions and anchorages for fast re-use, in road works and in concrete, even in severe weather conditions and at low temperatures. Quick anchoring of metal partitions and elements,grouts, equipment installation, street manhole covers, etc.
The surfaces should be clean and free of any soiling, crumbling and non-adhering parts, dust, salt efflorescence, milt of cement etc., free of oils, greases, properly hardened and compact. An adequate roughening of the surfaces by scarifying, sandblasting etc. is always necessary in order to obtain the maximum adhesion values to the substrate. The optimal values are obtained with high pressure hydro-scarification. Bare the irons undergoing disruptive oxidation or deeply oxidized, removing the rust of the exposed irons (by sandblasting or abrasive brushes).
Given the peculiarities of the product, it is advisable to adjust the mixing water as required from time to time, taking care not to make the product too fluid. Pour about 15% of water on the weight of the bag in the mixer, gradually add the product and the water still required, until the desired consistency is obtained. Continue to mix until a homogenous lump-free mixture is obtained.
- Brick trowel
- Finishing trowel
- Pour out
- Spatula
- Water
- Asphalt
- Concrete
The mortar should be laid within the specified time of workability, which may change depending on the temperature.
Want to know more about our products?
GROUT 2
It is a classic, self-levelling, castable motor, shrink-proof, for precision anchorage and fastening.
GROUT 6
Shrink-proof, castable mortar to use for fastening and anchorage of operating machinery or industrial structures with considerable filling thickness. The aggregate is bigger compared to GROUT 2.
GROUT 6 SFR
It is the fibre reinforced version with steel fibres of GROUT 6, specifically for structural installation of road joints, in road works.
GROUT CR
Product unique in its kind, specifically for structural blocks stacked, pillars or works in general in a marine environment, including submerged structures in fresh or salt water. Recommended!
GROUT 6 HP
It is the super performance version for precision anchors of GROUT 6, specifically designed for large anchors: wind towers, bollards for large ships, etc.