Rheoplastic, shrink-proof, fibre-reinforced mortar for precision anchorage

Code: GRT.0262

Components: 1

Appearance: Powder

GROUT 2 SFR is a high-performance, self-levelling castable mortar, being fibre-reinforced with READYMESH MM-150 steel fibres and READYMESH PM-060 polypropylene microfibres, with high flexural strength, great adhesion to concrete and steel, and shrinkage compensation. Aggregates with a maximum size of 2 mm. It is ideal for restorations, reinforcements and seismic adjustments, offering ductility for medium thicknesses (3–10 cm), on structures in reinforced concrete and masonry.

Linee di appartenenza

Certification obtained and Standards

Products and systems for the protection and repair of concrete structures - Structural and non-structural repair (R4)

EN 1504-3

Products and systems for the protection and repair of concrete structures - Structural and non-structural repair (R4)

General characteristics


Density: 2.200 kg/dm³


Max. recommended thickness: 15 cm


Maximum diameter of aggregate: 2 mm


Mix with water: 15 %




Pot-life: 30 min


Shelf-life: 12 months


Temperature of use: +5 / +35 °C

Technical specifications

Bonding force

2.4 MPa

Compressive strength

70 N/mm²

Compressive strength after 01 day

> 35 N/mm²

Flexural strength

10.3 N/mm²

Reaction to fire

A1 _

Available colours

- Gray

Packaging and dimensions

- Bag 25 kg

- Pallet: 50 x (Bag 25 kg)


Approximately 1900 kg of GROUT 2 SFR for every cubic metre of mixture to be made.

Use fields

Precision anchorage of operating machines: presses, turbines, power supply units, rolling mills, alternators, overhead cranes, metal structures, tracks, etc.. Structural adaptation, renovations, drawing and reinforcements, using injections and castings inside formworks. Creation of connection anchorage using steel bars with a diameter and depth consistent with the project specifications, by casting in specifically prepared perforations. Construction of structural road joints.

Preparation of supports

The application surfaces should be clean, free of containment, inconsistent and incoherent parts, dust, etc., conveniently saturated with water to reach the "saturated to dry surface" condition. An adequate roughening of the surfaces by scarifying, sandblasting etc. is always necessary in order to obtain the maximum adhesion values to the substrate. The optimal values are obtained with high pressure hydro-scarification. Bare the irons undergoing disruptive oxidation or deeply oxidized, removing the rust of the exposed irons (by sandblasting or abrasive brushes).

Use method

Place 2/3 (approx 2.5 litres per bag) of the total water in the mix, then gradually add the product and the remaining water, mixing until you obtain an even mix with the desired consistency and no lumps.

Application methods

- Pour out

Tool cleaning

- Water

Permitted supports

- Concrete

- Prefabricated concrete

- Mixed walls (bricks and stones)

- Rusty reinforcement rods

Warnings, precautions and Ecology

Given the self-levelling properties of the product and its self-compacting capacity, you are advised to pay due attention to the vibration phase. Excess zeal in the vibration operation could worsen the aesthetic performance of the resulting manufactured work.

Do not use in the absence of adequate side confinements.

Ensure protection and damp seasoning of the surfaces exposed.

Implement casting procedures capable of ensuring the absence of vacuums and cracks; grout the mortar from one part of the perimeter of the casting to avoid air sacks.

Contact us now

Want to know more about our products?

Attention, correctly compile this field.
Attention, enter a valid email address.
Attention, correctly compile this field.

By submitting I accept the privacy policy

Attention, correctly compile this field.

Subscribe to the newsletter


Products on display

  • Syntech Poliurea
  • Osmocem
  • Concrete Repar